| Item | Specifications |
| Color APHA | ≤60 |
| Viscosity 25℃mPa.s | 100~200 |
| Epoxy Value eq/100g | 0.65-0.70 |
| Epoxy Equivalent g/eq | 143~154 |
| Hydrolyzable chlorine eq/100g | ≤0.01 |
| Inorganic chlorine eq/100g | ≤0.005 |
| Moisture Content % | ≤0.1 |
Usage
Glycerol of glycerol contains three epoxy groups, and the crosslinking density is high. As a reactive diluent for epoxy resin, 5%-20% has good mechanical properties such as tensile strength, flexural strength, compressive strength and impact strength after curing. At the same time, it can reduce the viscosity of the system, improve the wettability of pigments and fillers, and have low volatility. It can also be used as a fiber wrinkle treatment agent, and for electronic sealing, coating, building adhesive and adhesives. It is also used as a crosslinking agent for polyurethane emulsion, 1-5%, as the main agent
Storage
It should be sealed and shaded to be stored in a dry, cool, well ventilated place.
| Item | Specifications |
| Color APHA | ≤60 |
| Viscosity 25℃mPa.s | 100~200 |
| Epoxy Value eq/100g | 0.65-0.70 |
| Epoxy Equivalent g/eq | 143~154 |
| Hydrolyzable chlorine eq/100g | ≤0.01 |
| Inorganic chlorine eq/100g | ≤0.005 |
| Moisture Content % | ≤0.1 |
Usage
Glycerol of glycerol contains three epoxy groups, and the crosslinking density is high. As a reactive diluent for epoxy resin, 5%-20% has good mechanical properties such as tensile strength, flexural strength, compressive strength and impact strength after curing. At the same time, it can reduce the viscosity of the system, improve the wettability of pigments and fillers, and have low volatility. It can also be used as a fiber wrinkle treatment agent, and for electronic sealing, coating, building adhesive and adhesives. It is also used as a crosslinking agent for polyurethane emulsion, 1-5%, as the main agent
Storage
It should be sealed and shaded to be stored in a dry, cool, well ventilated place.