Chemical name: diphenyl dihydrazide dihydrazide
Product name: Decanedioic acid, 1, 10-bis(2-benzoylhydrazide)
Molecular formula: C24H30N4O4
Molecular weight: 438.52
CAS No. :35658-27-6
Technical indicators
Appearance: white powder
Melting point: ≥200。C
Whiteness (R457): ≥90
Usage
TMC-300 is a nucleating agent for hydrazide-based polylactic acid (PLA). It has good compatibility with PLA resin, can be dissolved into polylactic acid melt at processing temperature, and crystallizes first during the cooling process of resin melt. And through the intermolecular self-assembly to form nano-scale fibrous crystals, induce the epigenetic crystal of PLA molecules, thereby achieving the purpose of accelerating the crystallization rate, shortening the molding cycle, and improving the heat resistance, flexural modulus and surface gloss of the product. In addition.
TMC-300 also has a good crystallization-promoting effect on crystalline aliphatic-based biodegradable polyesters such as polyalkanoate (PHAs) and polybutylene succinate (PBS). Based on the hydrazide structure in its molecule, this product has the effect of inhibiting and passivating the catalysis of the degraded metal ion (heavy metal ion) on the degradation of the polymer, thus showing a certain antioxidant performance.
The recommended amount of TMC-300 is 0.5- 1.5% by mass of the resin. When blended with resin pellets such as polylactic acid, other dispersing agents may be suitably used to promote uniform dispersion. This product can be directly used in the matrix resin, and can also be processed into a certain concentration of masterbatch.
Storage
It should be sealed and shaded to be stored in a dry, cool, well ventilated place.
Chemical name: diphenyl dihydrazide dihydrazide
Product name: Decanedioic acid, 1, 10-bis(2-benzoylhydrazide)
Molecular formula: C24H30N4O4
Molecular weight: 438.52
CAS No. :35658-27-6
Technical indicators
Appearance: white powder
Melting point: ≥200。C
Whiteness (R457): ≥90
Usage
TMC-300 is a nucleating agent for hydrazide-based polylactic acid (PLA). It has good compatibility with PLA resin, can be dissolved into polylactic acid melt at processing temperature, and crystallizes first during the cooling process of resin melt. And through the intermolecular self-assembly to form nano-scale fibrous crystals, induce the epigenetic crystal of PLA molecules, thereby achieving the purpose of accelerating the crystallization rate, shortening the molding cycle, and improving the heat resistance, flexural modulus and surface gloss of the product. In addition.
TMC-300 also has a good crystallization-promoting effect on crystalline aliphatic-based biodegradable polyesters such as polyalkanoate (PHAs) and polybutylene succinate (PBS). Based on the hydrazide structure in its molecule, this product has the effect of inhibiting and passivating the catalysis of the degraded metal ion (heavy metal ion) on the degradation of the polymer, thus showing a certain antioxidant performance.
The recommended amount of TMC-300 is 0.5- 1.5% by mass of the resin. When blended with resin pellets such as polylactic acid, other dispersing agents may be suitably used to promote uniform dispersion. This product can be directly used in the matrix resin, and can also be processed into a certain concentration of masterbatch.
Storage
It should be sealed and shaded to be stored in a dry, cool, well ventilated place.